0Cr21Al4 resistance wire is a type of iron chromium aluminum alloy
resistance wire, which has good high-temperature stability and
oxidation resistance, and is therefore widely used in many fields.
By being used in household appliances, 0Cr21Al4 resistance wire
provides users with efficient and stable heating solutions,
improving the performance and user experience of household
appliances.
0Cr21Al4 resistance wire is used as a heating element in ovens to
provide stable heating, ensuring even heating for better cooking
results.
0Cr21Al4 resistance wire is used as a heating element in water
heaters to quickly heat water and maintain a constant temperature,
providing users with comfortable hot water.
0Cr21Al4 resistance wire is used as a heating element in toaster
ovens to quickly heat up, making bread golden and crispy, providing
a delicious breakfast option.
0Cr21Al4 resistance wire is used as a heating element in coffee
machines to quickly heat water, allowing coffee to be brewed in a
short time while preserving its aroma and flavor.
0Cr21Al4 resistance wire is used as a heating element in induction
cooktops to provide efficient heating, quickly heating the cookware
to the desired temperature, achieving precise cooking.
- Ferrous Chromium Aluminum alloy performance tables
| Alloy Nomenclature Performance | 1Cr13Al4 | 0Cr25Al5 | 0Cr21Al6 | 0Cr23Al5 | 0Cr21Al4 | 0Cr21Al6Nb | 0Cr27Al7Mo2 |
| Main Chemical composition | Cr | 12.0-15.0 | 23.0-26.0 | 19.0-22.0 | 20.5-23.5 | 18.0-21.0 | 21.0-23.0 | 26.5-27.8 |
| Al | 4.0-6.0 | 4.5-6.5 | 5.0-7.0 | 4.2-5.3 | 3.0-4.2 | 5.0-7.0 | 6.0-7.0 |
| Re | opportune | opportune | opportune | opportune | opportune | opportune | opportune |
| Fe | Rest | Rest | Rest | Rest | Rest | Rest | Rest |
| | | | | | Nb0.5 | Mo1.8-2.2 |
| Max. continuous service temp. of element(°C) | 950 | 1250 | 1250 | 1250 | 1100 | 1350 | 1400 |
| Resistivity at 20ºC(μΩ·m) | 1.25 | 1.42 | 1.42 | 1.35 | 1.23 | 1.45 | 1.53 |
| Density(g/cm3) | 7.4 | 7.1 | 7.16 | 7.25 | 7.35 | 7.1 | 7.1 |
| Thermal conductivity(KJ/m·h·ºC) | 52.7 | 46.1 | 63.2 | 60.2 | 46.9 | 46.1 | |
| Coefficient of lines expansion(α×10-6/ºC) | 15.4 | 16 | 14.7 | 15 | 13.5 | 16 | 16 |
| Melting point approx.( ºC) | 1450 | 1500 | 1500 | 1500 | 1500 | 1510 | 1520 |
| Tensile strength(N/mm2) | 580-680 | 630-780 | 630-780 | 630-780 | 600-700 | 650-800 | 680-830 |
| Elongation at rupture(%) | >16 | >12 | >12 | >12 | >12 | >12 | >10 |
| Variation of area(%) | 65-75 | 60-75 | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 |
| Repeat Bending frequency(F/R) | >5 | >5 | >5 | >5 | >5 | >5 | >5 |
| Hardness(H.B.) | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 |
| Continuous Servicetime(Hours/ ºC) | -- | ≥80/1300 | ≥80/1300 | ≥80/1300 | ≥80/1250 | ≥50/1350 | ≥50/1350 |
| Micrographic structure | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite |
| Magnetic properties | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic |